タングステン粉 |
| 記号 | 粒度（μm） | 化学成分 ％ | ||||
| W | N.V.R. | Fe | Mo | O | ||
| W-H | 0.45～0.59 | ≧99.9 | ≦0.010 | ≦0.015 | ≦0.010 | ≦0.80 |
| W-1 | 0.60～0.99 | ≧99.9 | ≦0.010 | ≦0.015 | ≦0.010 | ≦0.60 |
| W-2 | 1.00～1.49 | ≧99.9 | ≦0.010 | ≦0.015 | ≦0.010 | ≦0.30 |
| W-3 | 1.50～1.99 | ≧99.9 | ≦0.010 | ≦0.015 | ≦0.010 | ≦0.15 |
| W-4 | 2.00～3.99 | ≧99.9 | ≦0.010 | ≦0.015 | ≦0.010 | ≦0.10 |
| W-5 | 4.00～7.99 | ≧99.9 | ≦0.010 | ≦0.015 | ≦0.010 | ≦0.10 |
| W-6 | 8.0～16.0 | ≧99.9 | ≦0.010 | ≦0.015 | ≦0.010 | ≦0.10 |
| 通常W粉の粒径写真 | |
 |
タングステン粉・均粒品 |
| 記号 | 粒度（μm） | 化学成分 ％ | ||||
| W | N.V.R. | Fe | Mo | O | ||
| W-1K | 0.60～0.99 | ≧99.9 | ≦0.010 | ≦0.015 | ≦0.010 | ≦0.60 |
| W-2K | 1.00～1.49 | ≧99.9 | ≦0.010 | ≦0.015 | ≦0.010 | ≦0.30 |
| W-3K | 1.50～1.99 | ≧99.9 | ≦0.010 | ≦0.015 | ≦0.010 | ≦0.15 |
| W-4K | 2.00～3.99 | ≧99.9 | ≦0.010 | ≦0.015 | ≦0.010 | ≦0.10 |
| 均粒品W粉の粒径写真 | |
 |
タングステン粉・単粒子品 |
| 記号 | 粒度（μm） | 化学成分 ％ | ||||
| W | N.V.R. | Fe | Mo | O | ||
| W-1KD | 0.60～0.99 | ≧99.9 | ≦0.010 | ≦0.015 | ≦0.010 | ≦0.80 |
| W-2KD | 1.00～1.49 | ≧99.9 | ≦0.010 | ≦0.015 | ≦0.010 | ≦0.30 |
| W-3KD | 1.50～1.99 | ≧99.9 | ≦0.010 | ≦0.015 | ≦0.010 | ≦0.20 |
| W-4KD | 2.00～3.99 | ≧99.9 | ≦0.010 | ≦0.015 | ≦0.010 | ≦0.15 |
| W-5KD | 4.00～7.99 | ≧99.9 | ≦0.010 | ≦0.015 | ≦0.010 | ≦0.10 |
| W-6KD | 8.0～16.0 | ≧99.9 | ≦0.010 | ≦0.015 | ≦0.010 | ≦0.10 |
| 単粒子W粉の粒径写真 | |
 |
タングステン粉・粗粒品 |
| 記号 | 粒度（μm） | 化学成分 ％ | ||||
| W | N.V.R. | Fe | Mo | O | ||
| W-L | 10.0～40.0 | ≧99.8 | ≦0.020 | ≦0.100 | ≦0.050 | ≦0.10 |
| W-S | -150 | ≧99.8 | ≦0.020 | ≦0.100 | - | ≦0.05 |
| 粒径写真 | |
 |
注意事項(※1) 粒度は、Sub Sieve Sizerによる平均粒度。但し、W-Sは篩い分け法による表示のみ。 (※2) タングステン純分は、100から、鉄、モリブデン、および不揮発分を差し引いた数値。 (※3) N.V.R.：不揮発分の略で780℃において塩化水素ガスで処理した残分(JIS H-1402) (※4) O：赤外線吸収法による分析値(JIS H-1402) (※5) タングステン粉は輸出管理規制品目です。 |