| WC | Mo2C | TiC | TaC | NbC | VC | ZrC | |
| Carbon content[%] (theoretical value) |
6.13 | 5.89 | 20.05 | 6.22 | 11.45 | 19.08 | 11.64 |
| Crystal structure | Hexagonal | Hexagonal | Face centerd cubic |
Face centerd cubic |
Face centerd cubic |
Cubic | Cubic |
| Lattice periods,kx. a | 2.906 | 2.997 | 4.3178 | 4.410 | 4.433 | 4.118 | 4.6828 |
| c | 2.837 | 4.727 | |||||
| c/a | 0.975 | 1.54 | |||||
| Density[g/cm3] calculated |
15.77 | 9.06 | 4.92 | 14.47 | 7.82 | 5.48 | 6.66 |
| experimental | 15.5-15.7 | 9.18 | 4.93 | 14.32 | 7.56 | 5.36 | 6.73 |
| Microhardness 100g [kg/mm2] |
1730 | 1479 | 2850-3200 (50g) | 1547 | 2055 | 2480 | 2950(50g) |
| Melting Point[℃] | 2600 | 2690±20 | 3250 | 3880±150 | 3500±125 | 2648 | 3530 |
| Heat of formation from the metal and carbon ΔH°(298） [Kcal/mol] |
-8.4±3.0 | -4.2 | -43.85 | -36.00 | -33.6±0.8 | -24.4±0.4 | -47.7±5.0 |
| Entropy S°(298) [Kcal/mol・℃] |
9.0±1.5 | 19.8±3.0 | 5.8±0.1 | 9.0±7.0 | 19.0±8.0 | 6.77±0.1 | 8.5±1.5 |
| Specific electrical resistance[μΩ・cm] at 20℃ |
19 | 71 | 61 | 22 | 44 | 78(25℃） | 49(25℃） |
| Point of transition to superconductivity °K |
2.5-4.2 | 2.9 | 11.15 | 7.6-9.5 | 10.1-10.5 | < 1.2 | < 1.2 |
（参考） データブック 高融点化合物便覧（モスクワ冶金出版所１９７６年版）
金属炭化物粉末は、代表的な硬質材料として 広範囲な用途が確立されています。 WCを主成分とする超硬合金は、70余年の歴史をもち、 切削工具や耐磨耗工具に用いられ、特性向上により ますます需要が拡大しています。 また、超硬合金には特性改良のための副成分として、 TiC、TaC（一般にはWC-MC固溶体）、 VC、Cr3C2などが添加されています。 TiCはサーメット切削工具の主成分であり、 他にTiN（TiC-TiN固溶体)、 NbC、VC、WC、Mo2C等も添加されます。 また、TiCはアルミナ系のセラミックス材や導電性添加剤として利用されます。 TaC、NbCは硬質時計側の装飾合金に、 WC、NbCは溶射など表面硬装用にもちいられ、 ZrCは赤外線放射特性に優れており、保温材などに採用されています。 |